ASTM/Asme A335/SA335 P1, P2, P5, P9, P11, P22, P23, P91, P92 Seamless Alloy Steel Pipe

• Customization: Available
• Technique: Hot Rolled
• Material: Alloy Steel
• Model NO.: ASTM/ASME A335/SA335 P1,P2,P5,P9,P11,P22,P23,P91
• Surface Treatment: Black
• Usage: Construction & Decoration
• Section Shape: Round
• A335 Material: ASTM A335 Gr. P5, P9, P11, P12, P21, P22 & P91
• Transport Package: Bundle, Wooden Box
• Trademark: C&N
• Origin: China
• Production Capacity: 1000tons/Month

Product Description

Description: Alloy steel pipe, alloy seamless steel pipe, alloy welded pipe,seamless alloy steel pipe,alloy pipe,alloy steel tube 
  
Standard:ASTM A335,JIS G3458,JIS A3462,DIN17175,GB5310,GB9948 
ASTM/AME  A335 P1/P5/P9/P11/P12/P22/ P91/P92 Seamless Ferritic Alloy-Steel Pipe for High-Temperature Service 
Material:ASTM A335 P2, ASTM A335 P12, ASTM A335 P11, ASTM A335 P22, ASTM A335 P5, ASTM A335 P91, ASTM A335 P92. 
Outside Diameter:6 mm~600mm 
Wall thickness:2mm~60mm 

 

 

Chemical Composition(%):
Grade	UNS Designation	Composition, %
		Carbon	Manganese	Phosphorus,	Sulfur	Silicon	Chromium	Molybdenum	Others
P1	K11522	0.10-0.20	0.30-0.80	0.025 max	0.025 max	0.10-0.50	---	0.44-0.65	---
P2	K11547	0.10-0.20	0.30-0.61	0.025 max	0.025 max	0.10-0.30	0.50-0.81	0.44-0.65	---
P5	K41545	0.15 max	0.30-0.60	0.025 max	0.025 max	0.50 max	4.00-6.00	0.45-0.65	---
P9	S50400	0.15 max	0.30-0.60	0.025 max	0.025 max	0.25-1.00	8.00-10.00	0.90-1.10	---
P11	K11597	0.05-0.15	0.30-0.60	0.025 max	0.025 max	0.50-1.00	1.00-1.50	0.44-0.65	---
P12	K11562	0.05-0.15	0.30-0.61	0.025 max	0.025 max	0.50 max	0.80-1.25	0.44-0.65	---
P15	K11578	0.05-0.15	0.30-0.60	0.025 max	0.025 max	1.15-1.65	---	0.44-0.65	---
P21	K31545	0.05-0.15	0.30-0.60	0.025 max	0.025 max	0.50 max	2.65-3.35	0.80-1.06	---
P22	K21590	0.05-0.15	0.30-0.60	0.025 max	0.025 max	0.50 max	1.90-2.60	0.87-1.13	---
P23	K41650	0.04-0.10	0.10-0.60	0.03	0.01	0.50 max	1.90-2.60	0.05-0.30	V 0.20-0.30
									Cb 0.02-0.08
									B 0.0005-0.006
									N 0.030 max
									Al 0.030 max
									W 1.45-1.75
P91	K91560	0.08-0.12	0.30-0.60	0.02	0.01	0.20-0.50	8.00-9.50	0.85-1.05	V 0.18-0.25
									N 0.030-0.070
									Ni 0.40 max
									Al 0.04 max
									Cb 0.06-0.10
P92	K92460	0.07-0.13	0.30-0.60	0.02	0.01	0.50 max	8.50-9.50	0.30-0.60	V 0.15-0.25
									N 0.03-0.07
									Ni 0.40 max
									Al 0.04 max
									Cb 0.04-0.09
									W 1.5-2.00
									B 0.001-0.006

Mechanical Properties

Data	Grade P11, P22, P5, P9	Grade P91	Grade P92
Tensile strength, min, (MPa)	415	585	620
Yield strength, min, (MPa)	205	415	440
Elongation, min, (%), L/T	30/20	20/	20/

 

Heat Treatment

A / N+T

N+T / Q+T

N+T

Material & Manufacture
Pipe may be either hot finished or cold drawn with the finishing heat treatment noted below.
Heat Treatment Requirements

Grade	Heat Treatment Type  P5, P9, P11, and P22	Normalizing Temperature Range F [C]	Subcritical Annealing or Tempering  Temperature Range F [C]
P5 (b,c)	Full or Isothermal Anneal
	Normalize and Temper	*****	1250 [675]
	Subcritical Anneal (P5c only)	*****	1325 - 1375 [715 - 745]
P9	Full or Isothermal Anneal
	Normalize and Temper	*****	1250 [675]
P11	Full or Isothermal Anneal
	Normalize and Temper	*****	1200 [650]
P22	Full or Isothermal Anneal
	Normalize and Temper	*****	1250 [675]
P91	Normalize and Temper	1900-1975 [1040 - 1080]	1350-1470 [730 - 800]
	Quench and Temper	1900-1975 [1040 - 1080]	1350-1470 [730 - 800]

 
Mechanical Tests Specified
Transverse or Longitudinal Tension Test and Flattening Test, Hardness Test, or Bend Test 
For material heat treated in a batch-type furnace, tests shall be made on 5% of the pipe from each treated lot. For small lots, at least one pipe shall be tested. 
For material heat treated by the continuous process, tests shall be made on a sufficient number of pipe to constitute 5% of the lot, but in no case less than 2 pipe.
Notes for Hardness Test: 
P91 shall not have a hardness not exceeding 250 HB/265 HV [25HRC].
Notes for Bend Test: 
For pipe whose diameter exceeds NPS 25 and whose diameter to wall thickness ratio is 7.0 or less shall be subjected to the bend test instead of the flattening test. 
Other pipe whose diameter equals or exceeds NPS 10 may be given the bend test in place of the flattening test subject to the approval of the purchaser. 
The bend test specimens shall be bent at room temperature through 180 without cracking on the outside of the bent portion.
Hydrostatic Test
The inside diameter of the bend shall be 1 inch [25 mm]. 
Each length of pipe shall be Hydro tested, at option of manufacture nondestructive electric testing can be used.